Título: Desenvolvimento de película biocompatível para cicatrização de feridas
Título(s) alternativo(s): Biomaterial based on bocaiúva oil, Acrocomia aculeata (jacq.) Lodd., and selenium nanoparticles in wound dressing applications
Autor(es): Duarte, Letícia Castellani
Primeiro Orientador: Domingues, Nelson Luís de Campos
Segundo Orientador: Moreno, Susana Elisa
metadata.dc.contributor.referee1: Rinaldi, Jaqueline de Carvalho
metadata.dc.contributor.referee2: Santos, Joyce Alencar
metadata.dc.contributor.referee3: Botelho, Kilça Tanaka
Resumo: O processo de cicatrização é complexo e tem despertado o interesse de pesquisadores para o desenvolvimento de materiais para curativo. O prolongamento do tempo de cura de uma ferida implica diretamente no custo do tratamento que envolve tanto o valor financeiro do tratamento quanto a incapacidade do paciente em realizar suas tarefas diárias. Busca-se, portanto, alternativas para o tratamento de feridas que possam ser de baixo custo e que apresentem alta efetividade. Objetivou-se neste estudo o desenvolvimento de biomaterial à base de quitosana e polivinilálcool contendo nanoparticulas de selênio, óleo de bocaiúva e glutaraldeído como reticulante para tratamento de feridas por apresentarem todas essas características anteriormente citadas. O óleo utilizado foi extraído da polpa dos frutos da bocaiúva colhidos no período de janeiro a março da safra de 2015. Foi realizado caracterização da polpa e do óleo por análises físico-químicas e infravermelho, estas análises demonstraram que o óleo obtido está dentro dos parâmetros preconizados pela legislação vigente e condiz com dados da literatura. Preparou-se 4 tipos de películas, uma contendo os polímeros quitosana e polivinilálcool, uma contendo os polímeros e óleo de bocaiúva, uma contendo os polímeros e nanopartículas de selênio e uma contendo os polímeros, óleo de bocaiúva e nanopartícula de selênio. Realizou-se a caracterização das películas por infravermelho, ultravioleta-visível e microscopia eletrônica de varredura. Os resultados indicaram que a matriz polimérica foi sintetizada através de ligações cruzadas entre a quitosana e o glutaraldeido, apresentando reticulados que indicam a permeabilidade da película. Para avliação da cicatrização foram realizadas duas excisões cirúrgicas na pele de camundongos Swiss com o emprego de um punch histológico, atingindo todas as camadas da pele. Os grupos experimentais consistiram de animais com as feridas sem tratamento e animais com as feridas tratadas com as películas. Os animais foram tratados nos tempos de dois, sete e quatorze dias. Após o tratamento os animais foram eutanasiados e realizou-se a biópsia do tecido para realização de testes posteriormente. Os resultados apontaram diminuição da contração da ferida nos grupos tratados com película contendo óleo e na película contendo selênio quando comparadas ao grupo que recebeu película controle, no mesmo período houve diminuição de infiltrado inflamatório para a película com nanopartícula de selênio. A avaliação quantitativa de colágeno apontou maior quantidade de colágeno na película com óleo de bocaiúva e nanopartícula de Selênio (POB+Se) sendo que com relação a colágeno tipo I a maior quantidade observada foi na película que contem nanopartícula de selênio (PSe) e colágeno tipo III na película com óleo e nanopartícula de Se (POB+Se). A propriedade antioxidante do selênio pode estar relacionada a produção de colágeno que depende de co-fatores (ferro ferroso, oxigênio molecular, α-cetoglutaraldeido e vitamina C) necessários para a hidroxilação enzimática do colágeno. Concluimos que a película desenvolvida contendo selênio e óleo de bocaiúva acelerara o processo de reparo celular com qualidade de fibras de colágeno.
Abstract: The healing process is complex and has aroused the interest of researchers in the development of curative materials. Extending the healing time of a wound directly implies the cost of treatment involving both the financial value of the treatment and the inability of the patient to perform their daily tasks. Therefore, it is sought alternatives for the treatment of wounds that may be of low cost and that present high effectiveness. The aim of this study was the development of biomaterial based on chitosan and polyvinylalcohol containing selenium nanoparticles, bocaiúva oil and glutaraldehyde as crosslinking agent for the treatment of wounds because they present all these characteristics previously mentioned. The oil used was extracted from the pulp of the fruits of the bocaiúva harvested from January to March of the harvest of 2015. The pulp and oil characterization was carried out by physicochemical and infrared analyzes, these analyzes demonstrated that the oil obtained is within the parameters recommended by the current legislation and consistent with data from the literature. Four types of films were prepared, one containing the polymers chitosan and polyvinylalcohol, one containing the polymers and bocaiva oil, one containing the polymers and nanoparticles of selenium and one containing the polymers, bocaiva oil and selenium nanoparticle. The films were characterized by infrared, ultraviolet-visible and scanning electron microscopy. The results indicated that the polymer matrix was synthesized by crosslinking between chitosan and glutaraldehyde, showing crosslinks indicating the permeability of the film. In order to evaluate healing, two surgical excisions were performed on the skin of Swiss mice using a histological punch, reaching all layers of the skin. The experimental groups consisted of animals with untreated wounds and animals with wounds treated with the films. The animals were treated at two, seven and fourteen days. After the treatment the animals were euthanized and tissue biopsy was performed for testing later. The results indicated a decrease in wound contraction in the groups treated with oil-containing film and in the selenium-containing film when compared to the group that received control film, in the same period there was decrease of inflammatory infiltrate for the film with selenium nanoparticle. The quantitative evaluation of collagen showed a higher amount of collagen in the film with bocaiúva oil and Selenium nanoparticle (POB + Se). In relation to type I collagen, the highest amount observed was the film containing selenium nanoparticle (PSe) and collagen type III on film with oil and Se nanoparticle (POB + Se). The antioxidant property of selenium may be related to the production of collagen that depends on cofactors (ferrous iron, molecular oxygen, α- ketoglutaraldehyde and vitamin C) required for the enzymatic hydroxylation of collagen. We conclude that the developed film containing selenium and bocaiúva oil will accelerate the cell repair process with collagen fiber quality.
Palavras-chave: Biotecnologia
Biotechnology
Selênio
Selenium
Acrocomia
Pele - ferimentos
Skin - Wounds and injuries
CNPq: CNPQ::CIENCIAS BIOLOGICAS
Idioma: por
País: Brasil
Editor: Universidade Federal da Grande Dourados
Sigla da Instituição: UFGD
metadata.dc.publisher.department: Faculdade de Ciências Biológicas e Ambientais
metadata.dc.publisher.program: Programa de pós-graduação em Biotecnologia e Biodiversidade
Citação: DUARTE, Letícia Castellani. Desenvolvimento de película biocompatível para cicatrização de feridas. 2018. 72 f. Tese (Doutorado em Biotecnologia e Biodiversidade) – Faculdade de Ciências Biológicas e Ambientais, Universidade Federal da Grande Dourados, Dourados, MS, 2018.
Tipo de Acesso: Acesso Aberto
URI: http://repositorio.ufgd.edu.br/jspui/handle/prefix/504
Data do documento: 14-Nov-2018
Aparece nas coleções:Doutorado em Biotecnologia e Biodiversidade

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
LeticiaCastellaniDuarte.pdf2,24 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.